Sika ViscoCrete-530 P High-performance superplasticizer/water reducer
APPEARANCE / COLOURS ：Slight yellow powder
PACKAGING :20 kg bags
CHEMICAL BASE : Modified polycarboxylates
DENSITY: 0.40~0.60 g/cm3(bulk density)
PH VALUE 9.0 ~12.0 (at +23℃, 40 % solution)
TOTAL CHLORIDE ION CONTENT % w/w ：≤0.1%
EQUIVALENT SODIUM OXIDE AS % Na2O ：≤3.0%
Please feel free to contact me for more details :
CONTACT : JOYCE
TEL:+86-18795982484
EMAIL:joyce@yaojietech.com
PACKAGING :20 kg bags
CHEMICAL BASE : Modified polycarboxylates
DENSITY: 0.40~0.60 g/cm3(bulk density)
PH VALUE 9.0 ~12.0 (at +23℃, 40 % solution)
TOTAL CHLORIDE ION CONTENT % w/w ：≤0.1%
EQUIVALENT SODIUM OXIDE AS % Na2O ：≤3.0%
Please feel free to contact me for more details :
CONTACT : JOYCE
TEL:+86-18795982484
EMAIL:joyce@yaojietech.com
Sika® ViscoCrete®-530 P is a high-performance superplasticizer and water
reducer in powder form based on Sika® ViscoCrete® polycarboxylate polymer
technology.
USES
Sika® ViscoCrete®-530 P is formulated for applications in systems with high
calcium sulfate content or pure gypsum binders. The product is especially
suitable for the production of dry-mixed mortars and concrete for applications
like:
▪ Floor screeds, self-leveling screeds and underlayments
▪ Grouts, non-shrink grouts, repair mortars, tile adhesives
▪ Building plaster, render, stucco, bonding/filling compound, molding plaster,
dental & medical plaster
▪ Self-compacting concrete
Sika® ViscoCrete®-530 P can be used in the following binder systems:
▪ Calcium sulfate binders (α- and β-hemihydrate,
natural/thermal/syntheticanhydrite)
▪ Ternary compounds (Portland cement + calcium aluminate cement +
calcium sulfate)
▪ Portland cement and cement blends, especially cement with high C3A,
sulfate and alkali content
CHARACTERISTICS / ADVANTAGES
The benefits of Sika® ViscoCrete® -530 P include:
▪ High water reduction (resulting in high density and strength)
▪ Excellent flowability (resulting in highly reduced placing- and compacting
efforts)
▪ Increased early strength development
▪ Improved shrinkage and creep behavior
▪ Reduced mixing times due to rapid adsorption
▪ Long-term stability enables long slump life
▪ Low influence on hydration
▪ Efficiency over a wide pH-range
▪ Compatible with other additives, e.g. citric acid
▪ Free of formaldehyde (unlike SNF/SMF) and ammonia